GC Fuji Plus RMGIC

A resin-modified glass ionomer luting cement that delivers strong adhesion, easy handling, moisture tolerance, and long-term fluoride release for dependable crown and bridge cementation.

Special Price ₹4,474.00 Regular Price ₹5,300.00 15.58% off

Brochure

Write a Review

Brand: GC

SKU

11192

Description

GC Fuji Plus RM GIC is a resin-modified glass ionomer luting cement engineered for dependable and stress-free cementation of crowns, bridges, inlays, onlays, posts, and core materials. Its combination of glass ionomer chemistry and resin technology ensures strong intrinsic adhesion, minimal film thickness, superior moisture tolerance, and long-term fluoride release. Fuji Plus delivers exceptional handling, snap-set behavior for easy excess removal, and outstanding marginal integrity, making it a preferred luting solution for clinicians worldwide.

Key Features

Intrinsic adhesion to tooth structure eliminates moisture-sensitive bonding steps.
Excellent compatibility with metal, resin, and silanated porcelain restorations.
Smooth, creamy consistency with 10-micron film thickness for precise seating.
Snap-set characteristic allows easy excess removal after 60 seconds.
Moisture-tolerant formula minimizes postoperative sensitivity.
Sustained fluoride release enhances long-term protection and marginal seal.
High cohesive strength from resin-modified technology.
Radiopaque formulation supports clear diagnosis and radiographic evaluation.

Packaging

1 × 15 g Powder
1 × 8 g (7 ml) Liquid
1 × 7 g (6.5 ml) Conditioner
Accessories included

Specification

Type: Resin Modified Glass Ionomer Luting Cement
Indications: Cementation of metal, PFM, resin, all-ceramic crowns; inlays; onlays; bridges; posts; cores
Powder/Liquid Ratio: 2.0 g / 1.0 g
Mixing Time: 20 seconds
Working Time: 2 minutes 30 seconds (at 23°C, from start of mixing)
Final Finishing Time: 4 minutes 30 seconds after seating
Composition (Liquid): HEMA 25–35%, UDMA <10%, Polyacrylic acid 20–30%, Distilled water 20–30%
Composition (Powder): Alumino-silicate glass 99%
Storage: 4–25°C, cool and dark place
Shelf Life: Powder – 3 years; Liquid – 2 years

Directions to use

Prepare the tooth surface and, if required, apply GC Fuji PLUS Conditioner.
Dispense powder and liquid using the recommended ratio (2.0 g / 1.0 g).
Mix for 20 seconds until a smooth, creamy consistency is achieved.
Apply cement to the internal surface of the restoration.
Seat the restoration firmly; ensure complete seating.
Wait 60 seconds from seating for snap-set to occur.
Remove excess cement easily with an explorer or scaler.
Allow the cement to fully set and proceed with final finishing after 4 minutes 30 seconds.
Avoid contact with skin, soft tissues, and eyes; rinse immediately if accidental contact occurs.